Hot-dip galvanized (galvanizing)

Hot-dip galvanized (galvanizing), also known as hot-dip galvanized, it is an effective anti-corrosion of the metal, mainly used in various sectors of the metal structure facilities. The rust steel immersed in liquid zinc melt around 500 ℃, steel members attached to the surface of the zinc layer, which play the purpose of anti-corrosion. Hot-dip galvanizing process: finished of Pickling - washing - plus help the bath - drying - hanging plating - cooling - Pharmaceutical - cleaning - polishing - completion of the hot-dip galvanizing, hot dip galvanized by the ancient method of hot-dipped development come since 1836, France had been used in industrial hot dip galvanized, has a history of 140 years. However, the hot-dip galvanizing industry the past three decades along with the rapid development and large-scale development of the cold-rolled steel strip.

 

With the discovery of the industrial, hot dip galvanized products have been applied to many areas, hot-dip galvanized advantage of the anti-corrosion service life for a long time, to adapt to the the antiseptic treatment method widely been very popular. Been widely used in power tower, communication tower, railway, road protection, light poles, marine components, construction steel structure components, substation ancillary facilities, light industry.

 

Principle: hot dip galvanized iron pieces cleaned, and then the solvent treatment, drying after immersion in liquid zinc, iron, and the reaction of molten zinc alloyed zinc layer, its processes: the skim - washing - pickling - the fluxing - drying - hot-dip galvanized - separation - cooling passivation.

 

Galvanizing alloy layer mainly depends on the thickness of the silicon content of the steel chemical composition, the rough degree of the size of the cross-sectional area of the steel surface of the steel, the temperature of the zinc pot, the zinc immersion time, the cooling speed, and the cold deformation.

 

Hot-galvanized advantages,

1, low-cost processing: hot-dip galvanized anti-rust lower cost than the cost of other paint coating;

2, Durable: standard hot dip galvanized rust thickness can be kept for 50 years or more in the rural environment, without having to patch; standard hot dip galvanized rust layer can be maintained for 20 years in the urban areas or offshore area, without having to patch;

3, good reliability: galvanized layer with steel is metallurgically bonded to become a part of the surface of the steel, and therefore more reliable coating persistent;

4, the toughness of the coating: zinc coating to form a special metallurgical structure, this structure can withstand transportation and use of mechanical damage;

5, full protective: plated parts each part can be plated with zinc, even in the recesses, sharp corners and hiding places can be fully protected;

6, saving time and effort: the the galvanizing process faster than other coating construction method, and can avoid the the brushing time required on site after installation.